High-energy ball milling and spark plasma sintering of molybdenum - lanthanum oxide (Mo-La2O3) and molybdenum – lanthanum zirconate (Mo-La2Zr2O7) composite powders

ČELKO, L.; TKACHENKO, S.; CASAS LUNA, M.; DYČKOVÁ, L.; BEDNAŘÍKOVÁ, V.; REMEŠOVÁ, M.; KOMAROV, P.; DEÁK, A.; BALÁŽ, M.; CRAWFORD, D.; DIAZ-DE-LA-TORRE, S.; BODOKU, E.; CIHLÁŘ, J. High-energy ball milling and spark plasma sintering of molybdenum - lanthanum oxide (Mo-La2O3) and molybdenum - lanthanum zirconate (Mo-La2Zr2O7) composite powders. INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2022, vol. 102, no. 105717, p. 1-13. ISSN: 0263-4368.

Abstract

The current study is focused on the preparation of Mo-10 vol%La2O3 and Mo-10 vol% La2Zr2O7 composite powders via low- and high-energy ball milling approaches as potential candidates for near-future high-temperature structural applications. The mechanical milling parameters play a critical role on the final powder's microstructure. When using the high-energy milling mode (using 800 rpm, ball-to-powder ratio (BPR) 100: 6), the homogeneous powder agglomerates are formed with refined laminated microstructure and more uniform ceramic phase distribution in both Mo-La2O3 and Mo-La2Zr2O7 systems compared to the powders produced by means of the low-energy milling mode (using 350 rpm, BPR 100: 6), where inhomogeneous powder mixture with less embedding of ceramic phases into Mo agglomerates was obtained. This study also focuses on the evaluation of high-temperature phase and microstructural stability of the produced composite powders treated at the temperature of 1300 °C under the different gaseous environments, including ambient, inert and reducing atmospheres. The Mo-10 vol% La2Zr2O7 composite powder exhibited better thermal stability during the high-temperature exposure in all tested atmospheres in comparison with the Mo-La2O3 composite powder, since it revealed less intensive formation of the intermediate phases, such as lanthanum oxymolybdates. Therefore, the Mo-10 vol% La2Zr2O7 composite powder was used further for consolidation by means of spark plasma sintering at 1600 °C. The successful production of Mo-La2Zr2O7 composite with homogeneous distribution of ceramic phase, the grain size about of 5 μm, and hardness of 3.4 GPa was not reported so far.